<noframes id="ps28c"><rt id="ps28c"></rt><noframes id="ps28c"><bdo id="ps28c"><bdo id="ps28c"></bdo></bdo><noframes id="ps28c"><rt id="ps28c"></rt><rt id="ps28c"></rt><rt id="ps28c"><rt id="ps28c"></rt></rt><rt id="ps28c"><delect id="ps28c"><delect id="ps28c"></delect></delect></rt><rt id="ps28c"><delect id="ps28c"></delect></rt> <noframes id="ps28c"><noframes id="ps28c"><rt id="ps28c"></rt><rt id="ps28c"></rt><rt id="ps28c"></rt><rt id="ps28c"><rt id="ps28c"><delect id="ps28c"></delect></rt></rt><noframes id="ps28c"><rt id="ps28c"></rt><noframes id="ps28c"><rt id="ps28c"><rt id="ps28c"></rt></rt><noframes id="ps28c"><noframes id="ps28c"><noframes id="ps28c"><noframes id="ps28c"><rt id="ps28c"><delect id="ps28c"><delect id="ps28c"></delect></delect></rt><rt id="ps28c"></rt> <noframes id="ps28c"><rt id="ps28c"></rt><rt id="ps28c"></rt><rt id="ps28c"><delect id="ps28c"><delect id="ps28c"></delect></delect></rt><noframes id="ps28c"><rt id="ps28c"><rt id="ps28c"></rt></rt><noframes id="ps28c"><rt id="ps28c"></rt><noframes id="ps28c"><rt id="ps28c"></rt><rt id="ps28c"></rt><noframes id="ps28c"><rt id="ps28c"></rt>

設為主頁 加入收藏

WD8070聚酰亞胺浸漬樹脂

一、主要組成

該產品由均苯四甲酸二酐和二氨基二苯基醚在強極性溶劑中反應生成聚酰胺酸樹脂,浸漆后經烘烤成型轉變為均苯型聚酰亞胺樹脂。

二、適用范圍

該產品適用于C級絕緣結構的特種電機、電器繞組的浸漬絕緣處理。

三、主要性能

1、該產品具有優異的耐高溫、耐化學腐蝕、耐γ射線性能,溫度指數不低于220,短時耐熱性可達350℃ 以上。該產品適用于C級絕緣結構的特種電機、電器繞組的浸漬絕緣處理。

2、該產品固化后具有優異的介電性能和耐冷媒性能,固化后燃燒時具有自熄性。

3、產品固化粘結強度高。

四、技術指標

序號

指標名稱

單位

指標

1

外觀

/

棕至棕紅色粘性透明

液體,無機械雜質。

2

固體量(200±2℃,2h)

%

10.0±1

3

粘度(23±2℃,4號粘度杯)

s

100~240

4

介電強度

常態

KV/mm

≥100

浸水24h

≥80

250

≥60

5

體積電阻率

常態

Ω·m

≥1.0×1012

浸水24h

≥1.0×1010

250

≥1.0×108


五、注意事項

1、本產品因粘度較大,適合于真空壓力浸漬工藝。如需調整產品粘度,必須使用該公司提供的專用稀釋劑,于相對濕度≤65%的環境下兌入并攪拌均勻。未經驗證,不可使用普通市售溶劑,否則產品性能可能會迅速下降。

2、從冷庫取出本產品時,應于室溫下放置足夠長的時間,使之溫度達到室溫,擦干包裝桶表面凝露的水分后,方可打開密封蓋,嚴防因凝露帶入水分,影響產品性能及貯存穩定性。